Controlling the ENIG Process for Optimum Efficiency and Performance


Reading time ( words)

Introduction

In last month’s Trouble in Your Tank, different levels of corrosion in the nickel deposit were presented. In addition, the suggestion was made that mid-phosphorous content EN process was more beneficial with respect to solderability, as opposed to a high phos content nickel deposit. Certainly, concerns with corrosion of the nickel (with lower phos) were allayed as long as the proper process controls were in place. Ideally, the ENIG process must provide the optimum in solder joint reliability while operating at the highest level of cost efficiency. All too often, process parameters that have the most influence on these critical attributes are poorly understood. An example of poor control is shown in Figure 1. The gold deposit has been removed in order to expose the electroless nickel surface.

It is very difficult to discern any anomalies in the nickel deposit without removing the gold. It is clear from the SEMs in Figure 1 that there is significant corrosion on the electroless nickel surface. Obviously, this is an unacceptable situation, and in order to prevent it one must work harder to optimize and control the electroless nickel-immersion gold process. Some of these factors will now be presented in detail.

Critical Electroless Nickel Features:

  1. Phosphorous content control in the electroless nickel deposit. Don’t underestimate this important parameter.
  2. Stabilizers in the EN solution influence phosphorous content in the deposit.
  3. Phos content has strong influence on solderability, immersion gold deposit thickness and potential for hyper-corrosion.

Let’s look at these points in a little more detail.

As I have written in this monthly column on many occasions, operating the chemical processes within the process window is the key to consistent and predictable performance. After all, your customers should expect no less from you. So with respect to #1 above, it is recommended that the EN process be able to maintain a reasonably tight window with respect to phos content through five metal (MTOs) turnovers in the nickel solution.

Read the full column here.


Editor's Note: This column originally appeared in the August 2014 issue of The PCB Magazine.

Share

Print


Suggested Items

Alex Stepinski: GreenSource Fabrication Update

01/22/2020 | Barry Matties, I-Connect007
Alex Stepinski gives an update on GreenSource, their acquisition of AWP, and their move to full production after some delays. Barry Matties and Alex also discuss automation and the difficulties in hiring in the U.S. and announces the decision to go to market with their recycling equipment in 2020.

Logistics Are Frank Lorentz’s Passion

01/21/2020 | Barry Matties, I-Connect007
Recently, Barry Matties had the chance to visit Ventec International Group’s German facility in Kirchheimbolanden (KIBO), where he met Frank Lorentz, Ventec’s general manager for the location. Logistics are clearly Frank’s passion. He lives and breathes it. If you spend any amount of time with him, that is abundantly clear. This interview with Frank was conducted after a tour of the KIBO site.

Calumet Electronics and Averatek Team Up on A-SAP

12/02/2019 | Nolan Johnson, PCB007
Nolan Johnson talks with Brian Hess of Calumet Electronics and Mike Vinson of Averatek about the new, insertable additive processes that the companies are working on together to help factories running primarily subtractive processes to quickly convert to very high-density interconnect (HDI) features, including trace and space from 2.5-mil line and space to 1-mil line and space and below.



Copyright © 2020 I-Connect007. All rights reserved.