As a part of series of studies on X-ray inspection technology to quantify solder defects in BGA balls, we have conducted inspection of three-level Package-on-Package (PoP) by using a new automated X-ray inspection (AXI) technology that is capable of 3D-CT imaging. The new results are compared with the results of earlier AXI measurements. It is found that 3D measurements offer better defect inspection quality, and reduce lower false call and escapes.


Package-on-Package (POP) devices are different from conventional SMT devices because they require solder attachments at different levels from the PCB surface. Their importance becomes even greater as PoPs are increasingly utilized in various types of assemblies because designers want to take advantage of 3D integration, to offer superior performances in their new products. Therefore, achieving the best possible PoP solder joint quality becomes important consideration for today’s PCBA manufacturers.

As solder joints in a PoP device cannot be inspected by optical means, X-ray inspection mostly is the only way to assure their quality nondestructively. Recently, automated X-ray inspection—AXI (AXI3, AXI4)—are found to have capabilities to detect not only solder bridge, missing ball, extra solder, and ball voiding defects, but also open/HIP for the bottom and top layers of POP. However, AXI images are not as clear as 2DX and planar CT (pCT). In this project, we used an AXI with pCT (AXI5) capability to characterize the solder defects in POP to explore improvement in inspection quality in a production environment.

The goal of this project is to evaluate the level of performance offered by different types of X-ray inspection equipment. It is better for the PCBA manufacturers to be able to test POP using AXI with pCT images. Getting unambiguous images with Pass/Fail result AUTO output are the obvious benefits. Our project consists of three phases: (1) Analytical comparison of images acquired by 2DX and AXI with pCT; (2) exploration of possibilities to optimize the AXI with pCT algorithms in order to improve the quality of defect detection; and (3) attempt to develop a process for AXI with pCT algorithm optimization.


With more and more PoP packages in production assemblies, achieving zero defects escape rate came to our focus in recent years. In early 2013, we faced the issue that some open defective pins on the top layer of POP were escaped from AXI. Therefore, we have been working with our engineers and X-ray vendors for this issue being resolved. In 2013, the best detecting coverage for open/HIP on the bottom layer was 85% with about 14,000+ false call PPM, and was about 50% defects detecting coverage with >30,000 false call PPM for the top layer of POP. It was not available to detect open / HIP on top layer with 3 layers POP from our AXIs that time.

However with many efforts for new software development, as well as Algorithms Threshold settings studies, good achievements were obtained in 2014. Both AXI 3 and AXI 4 have capabilities to detect open/HIP defects with three-layer PoP packages, and the average defects escaped is 4-8% with about 20,000+ false call PPM. The challenge was that getting clear image difference between good solder and bad solder pins while showing big separation between good and bad joints numerical data as measured by main Algorithm.

There was benefit to verify POP solder joints with AXI capabilities. Since November of 2013, we have not seen any defective pin on 3 layers POP from our SMT lines at Milpitas site after SMT process improvement. With the real-time AXI testing data feedback, we are confident with our SMT process. Because of our AXI machine on the line with high false call PPM and not clear different X-ray images between good solder joint and bad solder joint, therefore usually we use 2DX to verify the defective pins which called at AXI. In this way, we do rework only when it is real defect.


In this project, we use AXI 5 for POP X-ray inspection. The reason we choose AXI 5 is that it not only has AXI capabilities, but also offers CT capabilities at reasonably high speed. These features (AXI & pCT) should provide more benefits for our SMT lines.

1. Summary of Previous Experiments on AXI3, AXI4

The inspection quality of AXI not only depends on the AXI machine design, but also on the on the structural complexity of a given POP. Figure 1 illustrates the three-layer POP we utilized in this study, which is assembled on a customer board. We do not test middle interposer ball layer of the POP on AXI as no SMT process is required on these pins. The POP structural information is tabulated in Table 1.


Figure 1: Structure of 3 BGA layers POP on Customer Board

  • a1 (Substrate1) = 0.122 ±0.022 mm
  • a2 (Substrate 2) = 0.262 ±0.022 mm



The 2DX results are adopted as the reference for this POP AXI study. We use two parameters (Defect Escaped % and False Call PPM) to evaluate the AXI capability. Table 2 summarized the results from inspections by AXI 3, and AXI 4. The definitions of Defect Escaped % and False Call PPM are expressed by Equation 1, and Equation 2.

Equation 1:

Defect Escaped % = (Total # of Defect Escaped / Total # of Defects) x 100%

Equation 2:

False Call PPM = (Total # of False Call / Total # of Tested Pins) x 1,000,000

The 2DX, AXI3, and AXI 4 testing results are shown with pin locations in Figure 2. The cell colors are described as below.



Figure 2: The Test Results of POP Board from 2DX, AXI3, AXI4



Figure 3: X-ray images for Detected HIP, Good solder, False Call pins from 2DX, AXI3, and AXI4.

Figure 3 shows X-ray images for Defective HIP, Good solder, and False Call pins on top BGA ball layer of the POP from 2DX, AXI3, and AXI4, where green, red, and yellow colors stand for Good solder joint, HIP/Open defective pin, and False Call pin respectively. It is obvious to see difference for good solder and open solder on 2DX images. Based on the observed images, the big challenge in AXI is that there is no obvious difference visible between the images of good solder joint verses defective HIP/Open pins. It is also observed at both AXI3, and AXI4 machines.

Therefore, our previous AXI study showed that AXI 3 and AXI 4 have capabilities to test POP including three ball layers by full AUTO mode with focus images for different BGA layers on POP Package. Both AXI3 and AXI4 have capabilities to detect POP open, HIP defects with some level of success. There is no clear visual distinction between AXI images of good verses bad pins, especially when it comes to HIP/Open defects. The requirement to balance for Defect Escaped % and False Call PPM was our main focus issue for AXI with POP study, and looking forward to having characterization of solder defects in POP with AXI systems for inspection quality improvement. That is the driving factor to work on with AXI 5 which has AXI and pCT capabilities for the POP project.

In Part 2, the authors discuss the highlights of AXI with planar computer tomography (pCT).

Editor's Note: This paper has been published in the technical proceedings of IPC APEX EXPO.


Suggested Items

VJ Electronix: Automating the X-ray Inspection Process

05/04/2022 | Nolan Johnson, I-Connect007
VJ Electronix's Brennan Caissie shares the benefits of a new inspection tool that can be used on a variety of boards, with an automated system that takes the pressure off the manufacturing floor operators and can provide feedback all the way to the design process.

Dave Hillman on Living Your Passion

03/29/2022 | Barry Matties, I-Connect007
Barry Matties leads this engaging retrospective conversation with Dave Hillman, a Fellow, Materials and Process engineer at Collins Aerospace, who talks about mentorship, pandemic changes, and solder. “Soldering is soldering,” Dave says. “But how we do that keeps evolving in response to the new technologies and smaller packages.” What’s the key to his success and longevity? “Find your passion.” Here’s how he’s done it.

IPC’s Dieter Bergman Fellowship Award Presented to Bev Christian, HDPUG

03/14/2022 | Patty Goldman, I-Connect007
The Dieter Bergman IPC Fellowship Award is given to individuals who have fostered a collaborative spirit, made significant contributions to standards development, and have consistently demonstrated a commitment to global standardization efforts and the electronics industry. Bev Christian is a facilitator for the High Density Packaging User Group (HDPUG) and an adjunct associate professor in the Department of Mechanical and Mechatronics Engineering of the University of Waterloo, Waterloo, Ontario, Canada. In the past 31 years he has held positions at Nortel, BlackBerry, and CALCE; all in the areas of materials and failure analysis. Bev has never missed an IPC APEX EXPO since its inception. He is a member of 27 IPC committees and attends as time and the lack of clones allow.

Copyright © 2022 I-Connect007. All rights reserved.